Smalto 650 Alluminio - Nero
Silicone aluminium for high temperatures
It has an excellent anti - corrosive protection
It responds to specifications MM 681 P
Codice
0204 - 0205
description
Aluminium finish based on silicone resins for high temperatures.
Use
This product is used for the protection of products subjected to high temperatures directly on sand - blasted sheet or on surfaces treated with inorganic zinc plating.
Appearance of the film
Matt
Color
Aluminium
Components
1
Hardening
Physical hardening through evaporation of solvents and internal polymerization after heating.
Specific weight
0,980 gr/ml
Volume of solids
31%
Voc
556 gr/liter
Minimum thickness
60 - 80 micron
Estimated yield
5,1 m² / litre for a thickness of 60 microns
Temperature Resistance
450° C continuously or 600° C on inorganic zinc plating
Preparation of surfaces
New steel:
SA 2 sandblasting or brushing in order to have clean surfaces or prime with an inorganic zinc plating.
Old paints:
Remove old parts that are peeling off, brush and remove dust
SA 2 sandblasting or brushing in order to have clean surfaces or prime with an inorganic zinc plating.
Old paints:
Remove old parts that are peeling off, brush and remove dust
Flash point
Component A 34°C
Thinner 34°C
Thinner 34°C
Preparation of the product
Mix the product before the use and add the thinner
Component A 100
Synthetic thinner max 5 %
Component A 100
Synthetic thinner max 5 %
Environmental conditions
Ambient temperature: from + 5 to 40° C
Temperature of the support: > 10° C
Humidity: 0 - 85 %
In order to prevent the formation of condensation, it is necessary that the temperature of the substrate is at least 3° C above the dew point.
Temperature of the support: > 10° C
Humidity: 0 - 85 %
In order to prevent the formation of condensation, it is necessary that the temperature of the substrate is at least 3° C above the dew point.
Drying and hardening time
For the thickness of 60 microns
10°C: 6 hours Dry to touch, 48 hours Dry in depth
20°C: 3 hours Dry to touch, 24 hours Dry in depth
30°C: 2 hours Dry to touch, 10 hours Dry in depth
10°C: 6 hours Dry to touch, 48 hours Dry in depth
20°C: 3 hours Dry to touch, 24 hours Dry in depth
30°C: 2 hours Dry to touch, 10 hours Dry in depth
Time of overpainting
Minimum (hours): 10°C - 24 ore; 20°C - 12 hours; 30°C - 6 hours
Maximum: unlimited in the absence of contaminants
Maximum: unlimited in the absence of contaminants
Application
Brush, roller, spray
If you use the brush, you have to use nylon or natural bristle brushes.
If you use the roller, you have to use medium - haired rollers.
For the application, it is necessary to use the method of crossing coats
If you use the brush, you have to use nylon or natural bristle brushes.
If you use the roller, you have to use medium - haired rollers.
For the application, it is necessary to use the method of crossing coats
Shelf life
2 years in a cool and dry place (max 40° C)
Packs
Lt. 16 - Lt. 4 - Lt. 0,750