SPATOFLEX - SPATOLATO EXTRA ELASTICO FIBRATO

Code

0904AF

Description

Elastic quartz coating, for exteriors and interiors, made from thermoplastic acrylic resins, natural fibres, granular marble, which give the product after complete drying a permanent elasticity, water resistance to weathering and atmospheric agents; it is impervious for mildew and lichen. While leaving the wall transpire, it is a waterproof material.

Use

It is used when high resistant and elastic coating is desired. It has particular resistance to micro-macro clefts, a high degree of resistance to climate and atmospheric agents, a particular shock resistance. The addition of highly effective anti-mildew and anti-algae salts makes the coating impervious to any microorganisms.

Appearance of the film

Matt

Color

White and from colour chart

Component

1

Hardening

Physical hardening by evaporation of water and coalescence of the polymer.

Specific weight

From 1,380 gr/ml

Volume of solids

51%

VOC

20 gr/ liter

Vapor permeability coefficient:

V2

Water absorption:

W2

Adhesion

1.1 MPa

Degradation

1.3 MPa

Thermal conductivity

(10 dry) 1.17 W/m*k (tab.valore; P=50%)

Reaction to fire

Euroclass F

Film thickness

1 mm= 1000 micron
1,2 mm= 1200 micorn
1,5 mm= 1500 micron

Estimate yield

1 mm= Kg. 1,500 kg/mq (200).
0,7-1,2= Kg. 1,800 kg/mq. (270)
1,2 mm= Kg. 2,500 kg/mq. (300)
1,5 mm= Kg. 2,800 kg/mq. (400)

flash point

Component A > 114°C

Elongation%

200 for a dry thickness of 500 microns

Washability

> 10000 touches

Preparation of the surface

New: Remove dirt and efflorescence and prime with our underlay;
Old: Make sure that the old plaster is well bound and in the case of cracks treat the support with our FLEXIBLE PRIMER WITH FIBERS

Preparation of the product

Stir well before using.
For spatula applications the product must not be diluted.

Environmental conditions

Room temperature:          from + 5 to + 40°C
Surface temperature:       > 10°C
Humidity:                            0 – 85 %
To prevent the formation of condensation is necessary that the temperature of the substrate is at least 3 ° C above the dew point.

Drying time and hardening

For thickness of 200 microns              10°C            20°C             30°C
Dry to the touch                                      24                  6                   1    hours
Through drying                                       24                  8                   2

Waiting times for overcoating

Minimum (h)                                        10°C          20°C            30°C
                                                                  24              8                  3
Maximum    unlimited in the absence of contaminants

Application

Apply with steel trowel and smooth with a plastic float.

shelf life

1 year in a cool, dry place (max 40 ° C)

Packs

Comp A Kg. 24